摘要: |
为了研究材料强度、初始裂缝开度、初始缝长和轴向压应力对岩体水力劈裂临界水压力的影响,采用水泥砂浆作为岩体相似材料,进行岩体水力劈裂试验,探讨其水力劈裂破坏机理。试验结果表明,岩体水力劈裂临界水压力与材料强度和轴向压应力存在正相关关系,轴向压应力较材料强度对水力劈裂临界水压力影响大;水力劈裂临界水压力与初始裂缝开度、初始缝长呈负相关关系,初始缝长对水力劈裂临界水压力敏感性比初始裂缝开度大。随着缝内水压的增大,岩体初始裂缝的裂尖扩展,裂隙水流渗入到损伤劣化区,在裂隙水流的双重力学作用下,损伤区裂隙、孔隙扩展贯通形成宏观裂缝,宏观裂缝在缝内水流双重力学作用下,裂尖应力强度因子超过断裂韧度,岩体失稳破坏。 |
关键词: 岩体 水力劈裂 临界水压力 双重力学作用 |
DOI: |
分类号:TU457; TV313 |
基金项目:国家自然科学基金资助项目(51609073);江西省水利科技项目(KT201545);水利部土石坝破坏机理与防控技术重点实验室开放研究基金资助项目(YK915007);江苏省普通高校研究生科研创新计划项目(KYZZ15_0139,KYZZ16_0284) |
|
Experimental studies on influence factors and mechanism of critical water pressure of hydraulic splitting in rock mass |
LIU Detan1,2, SHEN Zhenzhong1,2, XU Liqun1,2, QIU Liting1,2, JIANG Ting1,2
|
1.State Key Laboratory of HydrologyWater Resources and Hydraulic Engineering, Hohai University, Nanjing;2.College of Water Conservancy and Hydropower, Hohai University, Nanjing
|
Abstract: |
In order to investigate the impacts of material strength, initial crack opening, initial slit length, and the axial compressive stress on the critical water pressure for hydraulic splitting of the rock masses, the cement mortar is selected as the substitute material for a rock mass, and it is subjected to hydraulic splitting tests to examine its hydraulic splitting mechanism. The experimental analysis results indicate that a positive correlation exists between the critical water pressure for the hydraulic splitting and the material strength and the axial compressive stress of the rock mass. The axial compressive stress is found to have a larger impact on the critical water pressure for the hydraulic splitting than that of the material strength. However, the critical water pressure for the hydraulic splitting has a negative correlation with both the initial crack opening and the initial slit length, with the latter being more sensitive to the critical water pressure for the hydraulic splitting than the former. When the water pressure in the rock cracks increases, the tip of the initial crack expands and allows more fissure water to infiltrate the damaged and degraded zone. Under the dual mechanical effects of fissure water, the fractures and pores in the damaged zone expand and interconnect to form macrocracks. These macrocracks are in turn subjected to similar dual mechanical effects. Eventually, the stress intensity factor at the tip exceeds the tenacity of the cracks, resulting in destabilization and destruction of the rock mass. Under the action of the double mechanics of water flow in the rock, the stress intensity factor of the crack tip exceeds the fracture toughness, and the rock mass is unstable. |
Key words: rock mass hydraulic splitting critical water pressure double mechanical effects |