摘要: |
对水泥-靡细矿渣胶凝体系水化产物-F盐的微观结构试验表晨,F盐的X射线衍射强度峰出现在最大晶面距d=80nm附近,吸热峰出现在360℃左 右,其六方片状晶体的尺寸约为2-3um。此外,分析了影响F盐生成的因素,籍此解释了大掺量磨细矿渣胶凝体系 具有优越的 氯离子经生能的原因。 |
关键词: 磨细矿渣 水化产物 微结构 水工结构 钢筋混凝土 水泥 |
DOI: |
分类号:TV421.5 |
基金项目:九五”国家科技攻关项目(96-415-04-03) |
|
Microstructure analysis onFriedel's salt in hydrate of cement and GGBS |
CAI Yue bo,LUO Rui,WANG Chang yi
|
Abstract: |
The microstructure of Friedel's (F) salt in hydrate of cement andgranulated ground blast furnace slag (GGBS) is experimentally studied. It can be seen that the maximum XRD-intensity of F salt appears at 80 nm and that an endothermic effect yields at around 360℃. The morphology of F salt is a hexagonal slice with a size of 2~3 micrometers. The influence of F salt's formation is analyzed, and the mechanism of chloride binding capability of cement with great volumes of GGBS is also explained. |
Key words: granulated ground blast furnace slag(GGBS),hydrate,Friedel's salt,microstructure |